This paper aims to study the possibility of electroplating copper coatings on chemically and chemical-galvanically nickel-plated acrylic fibers, to be further processed into yarn, fabrics, knitwear and nonwoven materials.

Electrically conductive fibers with different copper contents have been obtained, and the effect of electrolyte pH, its composition, current strength at the first and second cathodes, as well as the metallization time on the electrophysical, physical and mechanical properties of copper-containing fibers, has been studied.

The studies have shown that with an increase in the copper content, the electrical conductivity, the uniformity of the coating and the uniformity of the electrophysical properties (for chemical-galvanically nickel-plated fiber) increase. In the case of copper plating of chemically nickel-plated fiber, the coefficient of variation in electrical resistance increases with increasing plating time, even though the copper content increases, and the coefficient of variation in copper content and electrical resistance decreases. The physical and mechanical properties of copper-containing fibers differ slightly from the original (subjected to copper plating) and industrial Nitron fibers. With copper plating, the strength of the fiber practically does not decrease, and the elongation decreases somewhat, compared with the mass-produced Nitron fiber.

The physical and mechanical properties of copper-containing fibers are quite high, which makes it possible to be successfully further processed into yarn, fabrics, knitwear and nonwoven materials.

This study aims to investigate the effects of the number of miss stitches and tuck stitches in the knit structure on the technological parameters and physical and mechanical properties of knitted fabrics.

The number of miss stitches and tuck stitches was increased from 3.6% to 8.3%, and the influence of this increase on knitwear properties was analyzed.

It was found that an increase from 3.6% to 8.3% leads to a decrease in the stretchability of knitwear in width from 330% to 290% and in length from 112% to 95%. With an increase from 5% to 6.3%, the surface density of knitwear decreases by 11.6 g. And with an increase from 6.3% to 8.3%, the surface density of knitwear decreases by 11.8 g. It was also found that the presence of miss stitches and tuck stitches in the knit structure reduces the material consumption, and the presence of miss stitches increases the shape stability of the knitted fabric.

It was concluded that the number of miss stitches and tuck stitches has the strongest influence on surface density, followed by volume density.